GEOMEMBRANE

 
     
  Geomembranes Essentially impermeable sheets produced from polymeric materials. Geomembranes are manufactured several ways, excluding woven methods as they would leave unacceptably large voids in the material. Suitable materials include PVC, Polypropylene, Polyethylene and HDPE  
     
 

APPLICATION

PRIMARY FUNCTION

Hazardous Solid Waste Land Filled

Impervious barrier

Municipal Solid Waste Land Filled

Impervious barrier

Road Work

Impervious barrier

Air Field

Impervious barrier

Water Reservoir

Impervious barrier

Evaporation Pond 

Impervious barrier

Land Filled Capping

Impervious barrier

 
     
 

Specification of High Density PolyEthylene (HDPE) GeoMembrane

 
 

Property

Test Method

Nominal Values

Thickness, mm

ASTM D 751/1593/5199

1.0

1.5

2.0

2.5

3.0

Density, g/cc

ASTM D 792/1505

0.94

0.94

0.94

0.94

0.94

Strength at Break, N/mm

ASTM D 6693, Type IV

34

52

69

86

103

Strength at Yield, N/mm

ASTM D 6693, Type IV

16

25

33

41

50

Elongation at Break, %

ASTM D 6693, Type IV

750

800

800

800

800

Elongation at Yield, %

ASTM D 6693, Type IV

15

15

15

15

15

Tear Resistance, N

ASTM D 1004

146

222

293

369

445

Puncture Resistance, N

FTMS 101, Method 2065

267

400

533

667

800

Carbon Black Content, %

ASTM D 1603

2-3

2-3

2-3

2-3

2-3

Carbon Black Dispersion

ASTM D 3015

A1/A2

A1/A2

A1/A2

A1/A2

A1/A2

Dimensional Stability, % (each direction)

ASTM D 1204, 100°C 1hr

±1

±1

±1

±1

±1

Environmental Stress Crack Resistance, hr

ASTM D 1693, Cond. B

>2000

>2000

>2000

>2000

>2000

Low Temperature Brittleness, °C

ASTM D 746, Cond. B

<-84

<-84

<-84

<-84

<-84

Oxidative Induction Time, minutes

ASTM D 3895, 200°C Pure O2, 1 atm

100

100

100

100

100

Ozone Resistance

ASTM D 1149, 7 days 100ppm

No Cracks

No Cracks

No Cracks

No Cracks

No Cracks

Water Absorption, % wt. change

ASTM D 570

<0.01

<0.01

<0.01

<0.01

<0.01

Moisture Vapour Transmission, g/m²

ASTM E 96

<0.001

<0.001

<0.001

<0.001

<0.001

Melt Flow Index, g/10 minutes

ASTM D 1238, Cond. 190/2.16

<=1.0

<=1.0

<=1.0

<=1.0

<=1.0